CASIS Nitrile Insertion Rubber Sheet is a premium grade synthetic rubber made from 100% Nitrile polymer. It is specifically designed to display superior resistance to petroleum based fuids. This makes our Nitrile Insertion suitable for applications with long term exposure to fuel, oil and general hydrocarbons. Our Insertion has excellent physical properties including good mechanical strength. It displays good temperature resistance.
CASIS Insertion Rubber is reinforced with a nylon monofilament fabric for superior tear strength and dimensional stability.
CASIS Nitrile Insertion Rubber will also display resistance to a wide range of chemicals, acids and alkalis.
Fabric Reinforced Rubber Sheet
Use in hydraulics and where air, water or low pressure steam will be passed.
Oil resistance and where hot and/or cold water and gases are being transfered. Such applications might include meters, control devices, regulators, pumps and diaphragms. Resistance to oil, caustics, and aliphatic hydrocarbons.
Features:
Fabric Reinforced Rubber Sheet is a rubber sheet material that has been reinforced with one or more plies of cloth or duck such as polyester, nylon, and cotton or fiberglass fabric. This reinforcement gives added stability in flanged gasket applications requiring mechanical fastenings and reduces creep when there are high compression loads.
Specifications:
|
Polymer |
NBR |
|
|
Reinforcement |
Nylon |
|
|
Colour |
Black |
|
|
Specific Gravity |
1.20 |
ASTM D297 |
|
Hardness |
65° ± 5° Shore A |
ASTM D2240 |
|
Abrasion |
275mm3 (max) @ 10N |
ASTM D5963 |
|
Tensile Strength |
15 MPa (min ) |
ASTM D412 |
|
Elongation @ Break |
400% (min) |
ASTM D412 |
|
Compression Set |
30% |
ASTM D395 B |
|
Tear Strength |
40 N/mm (min) |
ASTM D624 |
|
Temperature Range |
-25°C to +90°C |
|
|
Standard Thickness |
1.0mm, 1.5mm, 3mm, 5mm, 6mm, 8mm, 10mm |
|
Standard Roll Size |
1200mm X 10M |
|
Cut lengths, strips and custom shapes are available upon request |